Dylon® A-8000SE
热塑性聚氨酯弹性体（聚酯）
Dahin Group 

Technical Data

产品说明

Dylon thermoplastic polyurethane elastomer combines the property pattern of high quality PU elastomers with the processing efficiency of thermoplastics. With its excellent elasticity, low temperature resistance, mechanical properties, and resistance to water and solvents, Dylon is widely used in injection molding and extrusion processing. Furthermore, it is exposing its wide applications as special grades TPU being developed according to customized purposes. As a result, Dylon TPU is becoming the most welcomed material to processing industries.

Applications of A-8000SE include film, electric cables and wires, and packaging seal.

总体

材料状态 • 已商用：当前有效    
供货地区 • 北美洲    
性能特点 • 防潮性 • 抗溶解性   
 • 高弹性 • 可加工性，良好  
    
用途 • 薄膜 • 电线电缆应用  
形式 • 颗粒料    
加工方法 • 挤出 • 挤出吹塑成型  
     
物理性能   额定值 单位制 测试方法 
比重   1.20g/cm³ ASTM D792 
弹性体   额定值 单位制 测试方法 
拉伸应力    ASTM D412 
100%应变   4.41MPa  
300%应变   7.86MPa  
抗张强度 (断裂)   29.6MPa ASTM D412 
伸长率 (断裂)   650% ASTM D412 
硬度   额定值 单位制 测试方法 
硬度计硬度 (邵氏 A)   80 ASTM D2240 
     
挤出   额定值 单位制  
干燥温度  82.2 到 104°C  
干燥时间  2.0 到 4.0hr  
建议的最大水分含量   0.030%  
第1气缸区温度  171 到 182°C  
第2气缸区温度  182 到 193°C  
连接器温度  193 到 199°C  
熔体温度  193 到 199°C  
模具温度  193 到 199°C  

备注
1 一般属性：这些不能被视为规格。